Also name:Grade 2 titanium plate ,Grade 2 titanium sheet.


We can supply Commercially pure titanium grade 2 specifications as follows:

Thickness: 0.5-70 mm

The width:≤ 2000 mm

The length:≤ 6000 mm

Special requirements can be customized as customer’s requirement

Standard : ASTM B265  ASME SB265 ASTM F67  AMS 4911

Test report: MA, SGS,  etc

Brand name: WIT


Commercially pure titanium grade 2 sheet features:

1. GR2 titanium plate is higher purity in pure titanium plate. Its ductility is slightly lower than Grade 1 titanium plate, and its hardness is slightly higher than Grade 1 titanium plate.

2. The purity is slightly lower than Grade 1 titanium plate, and the corrosion resistance is between Grade 1 titanium plate and Grade 3 titanium plate.

3. Higher physical and mechanical properties than GR1 titanium plate

4. Non-toxic, non-magnetic, no radiation, good biocompatibility.


Mechanical Properties

Grade

Tensile strength, MPa  (min)

Yield strength, MPa  (min)

Elongation, %(min)

Reduction of Area, %(min)

Gr2

345

275-450

20

-

Chemical Component

Grade

Ti

N,

max

C,

max

H,

max

Fe,

max

O,

 max

Residuals

Max  each

Max

  total

Gr2

Main

0.03

0.08

0.015

0.30

0.25

0.1

0.4

 

Application fields:

1.  Chemical industry.

2.  Electric power.

3.  Navigation.

4.  Medical and surgical implantation.

5.  Other fields which require slightly higher physical performance to make equipment or accessories


Product picture


The artcraft of process titanium sheet:

Hot forging :A process of forging above the recrystallization temperature of a metal.

Hot rolling:A process of rolling at temperatures higher than recrystallization.

Cold rolling:A process in which the plastic deformation temperature is lower than the recovery temperature.

Annealing:  A process by which a metal is heated slowly to a certain temperature, held for sufficient time, and then cooled at a suitable rate, usually slowly, and sometimes controllably.

Pickling: to remove thin films such as oxides from the surface of a metal by immersing the product in an aqueous solution such as sulfuric acid.Is electroplating, enamel, rolling and other processes of pre - treatment or intermediate treatment



http://www.wit-titanium.com/

Total0bar [View All]  Related Comments
 
more»Other products

[ Products search ] [ favorites ] [ Tell friends ] [ Print ] [ Close ]